Plastics & flame retardants
Modified PA66
Modified Plastics
Modified Plastics
Modified PA66
MATERIAL OVERVIEW
GREPLAS®
Typical Applications
Automotive: fuse boxes, connectors, charging gun plugs and sockets, high-voltage connectors, radiator tanks, brackets, bearing retainers, cable ties, insert-molded parts, and metal-to-plastic replacements, etc.
Electronic and electrical: power supply bases, AC contactors, busbar bases, solenoid valves, etc.
Cable tie special grade.
Battery pack high-voltage wiring board, high-voltage connector, terminal block, automotive fuse box
| Properties | Unit | Test Method | Reinforced PA66 | |||
| GREPLAS® | GREPLAS® | GREPLAS® | GREPLAS® | |||
| Density | g/cm3 | ISO 1183 | 1.23 | 1.36 | 1.37 | 1.57 |
| Water Absorption | % | ISO 62 | 1.8 | 1.6 | 1.5 | 1.0 |
| Filler Content | % | ISO 3451-4 | 15 | 30 | 33 | 50 |
| Molding Shrinkage | % | ISO 294-4 | 0.7-1.1 | 0.3-0.7 | 0.3-0.6 | 0.1-0.4 |
| Melt Flow Rate | g/10min | ISO 1133-1:2011 | — | — | — | — |
| Tensile Strength | MPa | ISO 527-2 | 130 | 180 | 190 | 225 |
| Flexural Strength | MPa | ISO 178 | 190 | 250 | 260 | 340 |
| Flexural Modulus | MPa | ISO 178 | 5800 | 9000 | 8500 | 15000 |
| Notched Izod Impact Strength (23℃) | kJ/m2 | ISO 180 | 8 | 14 | 15 | 18 |
| Notched Izod Impact Strength (-40℃) | kJ/m2 | ISO 180 | — | — | — | — |
| Unnotched Charpy Impact Strength (23℃) | kJ/m2 | ISO 179 | 65 | 85 | 80 | 90 |
| Heat Deflection Temperature (1.80 MPa) | ℃ | ISO 75-2/A | 235 | 235 | 245 | 250 |
| Melting Temperature | ℃ | ISO 11357-1/-3 | 263 | 263 | 263 | 263 |
| Flame Rating (1.6 mm) | class | UL 94 | HB | HB | HB | HB |
| Flame Rating (0.8 mm) | class | UL 94 | — | — | — | — |
| Glow-Wire Flammability Index (GWFI) 2.0 mm | ℃ | IEC60695-2-12 | — | — | — | — |
| Comparative Tracking Index (CTI) | V | IEC 30112 | — | — | — | — |
| Surface Resistivity | Ohm.cm | IEC 60093 | 1.00E+14 | 1.00E+15 | 1.00E+15 | 1.00E+14 |
| Volume Resistivity | Ohm | IEC 60093 | 1.00E+13 | 1.00E+14 | 1.00E+14 | 1.00E+13 |
| Properties | Unit | Test Method | Flame-Retardant PA66 | Toughened PA66 | ||||
| GREPLAS® | GREPLAS® | GREPLAS® | GREPLAS® | GREPLAS® | GREPLAS® | |||
| Density | g/cm3 | ISO 1183 | 1.53 | 1.43 | 1.15 | 1.14 | 1.08 | 1.08 |
| Water Absorption | % | ISO 62 | 1.5 | 1.5 | 2.0 | 1.8 | 1.8 | 1.8 |
| Filler Content | % | ISO 3451-4 | 30 | 30 | — | — | — | — |
| Molding Shrinkage | % | ISO 294-4 | 0.2-0.5 | 0.2-0.5 | 1.1-1.4 | 1.0-1.4 | 1.2-1.6 | 1.2-1.6 |
| Melt Flow Rate | g/10min | ISO 1133-1:2011 | — | — | — | 30 | 15 | 25 |
| Tensile Strength | MPa | ISO 527-2 | 180 | 155 | 75 | 70 | 48 | 45 |
| Flexural Strength | MPa | ISO 178 | 250 | 230 | 110 | 85 | 52 | 52 |
| Flexural Modulus | MPa | ISO 178 | 9000 | 9000 | 3200 | 2200 | 1250 | 1400 |
| Notched Izod Impact Strength (23℃) | kJ/m2 | ISO 180 | 12 | 10 | 4.5 | 8 | 85 | 75 |
| Notched Izod Impact Strength (-40℃) | kJ/m2 | ISO 180 | — | — | — | — | 17 | 15 |
| Unnotched Charpy Impact Strength (23℃) | kJ/m2 | ISO 179 | 70 | 70 | 75 | NB | NB | NB |
| Heat Deflection Temperature (1.80 MPa) | ℃ | ISO 75-2/A | 225 | 238 | 65 | 62 | 65 | 47 |
| Melting Temperature | ℃ | ISO 11357-1/-3 | 263 | 263 | 263 | 263 | 263 | 263 |
| Flame Rating (1.6 mm) | class | UL 94 | V-0 | V-0 | V-0 | HB | HB | HB |
| Flame Rating (0.8 mm) | class | UL 94 | — | — | V-0 | — | — | — |
| Glow-Wire Flammability Index (GWFI) 2.0 mm | ℃ | IEC60695-2-12 | 960 | 960 | 960 | — | — | — |
| Comparative Tracking Index (CTI) | V | IEC 30112 | 250 | 550 | 600 | — | — | — |
| Surface Resistivity | Ohm.cm | IEC 60093 | 1.00E+14 | 1.00E+15 | 1.00E+14 | 1.00E+14 | 1.00E+15 | 1.00E+15 |
| Volume Resistivity | Ohm | IEC 60093 | 1.00E+13 | 1.00E+14 | 1.00E+13 | 1.00E+13 | 1.00E+14 | 1.00E+14 |
Product inquiry
Send the model code and we will confirm the details.
Quote the series above together with the quantity, application and required material behavior.